In-situ Observations of the Effect of the ZDDP Tribofilm Growth on Micropitting
It is found that oils with higher ZDDP concentrations produce more micropitting but less surface wear and that, at a given concentration, a mixed primary-secondary ZDDP results in more severe micropitting than a primary ZDDP. Too rapid formation of a thick antiwear tribofilm early in the test serves to prevent adequate running-in of sliding parts, which subsequently leads to higher asperity stresses and more asperity stress cycles and consequently more micropitting. Therefore, any adverse effects of ZDDP on micropitting and surface fatigue in general are mechanical in nature and can be accounted for through ZDDP’s influence on running-in and resulting asperity stress history. The observed correlation between antiwear film formation rate and micropitting should help in the design of oil formulations that extend component lifetime by controlling both wear and micropitting damage.